| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| 密度 | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | |
| 吸水率 |
0.15 %
@Time 86400 sec
|
0.15 %
@Time 24.0 hour
|
ASTM D570 |
| 水分吸收 | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| 平衡吸湿 | 0.35 % | 0.35 % | ASTM D570 |
|
0.58 %
@Temperature 100 °C
|
0.58 %
@Temperature 212 °F
|
ASTM D570 | |
| 饱和吸水率 | 0.35 % | 0.35 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
|
0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0050 - 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method | |
| 线性成型收缩率，横向 |
0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0050 - 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| 熔体流动速率 |
7.0 g/10 min
@Load 1.20 kg, Temperature 300 °C
|
7.0 g/10 min
@Load 2.65 lb, Temperature 572 °F
|
ASTM D1238 |
|
112.2 g/10 min
@Load 5.00 kg, Temperature 300 °C
|
112.2 g/10 min
@Load 11.0 lb, Temperature 572 °F
|
ASTM D1238 | |
| 化合物熔体指数 |
7.0 g/10 min
@Load 1.20 kg, Temperature 300 °C
|
7.0 g/10 min
@Load 2.65 lb, Temperature 572 °F
|
MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | 70 | 70 | ASTM D785 |
| 洛氏硬度（R 级） | 118 | 118 | ASTM D785 |
| 抗张强度(断裂) | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 135 % | 135 % | Type I, 50 mm/min; ASTM D638 |
| 140 % | 140 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D638 | |
| 拉伸模量 | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| 2.31 GPa | 335 ksi | 5 mm/min; ASTM D638 | |
| 弯曲强度 | 95.0 MPa | 13800 psi | 2 mm/min; ISO 178 |
| 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 2.25 GPa | 326 ksi | 2 mm/min; ISO 178 |
| 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 9.07 J/cm | 17.0 ft-lb/in | ASTM D256 |
|
1.39 J/cm
@Temperature -30.0 °C
|
2.60 ft-lb/in
@Temperature -22.0 °F
|
ASTM D256 | |
| 悬壁梁无缺口冲击强度 | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 |
| 悬壁梁缺口冲击强度 | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1A |
|
12.0 kJ/m²
@Temperature -30.0 °C
|
5.71 ft-lb/in²
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A | |
| 简支梁缺口冲击强度 | 9.50 J/cm² | 45.2 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 拉伸冲击强度 | 630 kJ/m² | 300 ft-lb/in² | Type S; ASTM D1822 |
| 落锤总能量 | 64.0 J | 47.2 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 169 J | 125 ft-lb | ASTM D3029 | |
|
65.0 J
@Temperature 23.0 °C
|
47.9 ft-lb
@Temperature 73.4 °F
|
ASTM D3763 | |
| 泰伯磨损，毫克/1000次 | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D257 |
| 介电常数 |
2.96
@Frequency 1.00e+6 Hz
|
2.96
@Frequency 1.00e+6 Hz
|
ASTM D150 |
|
3.17
@Frequency 50.0 - 60.0 Hz
|
3.17
@Frequency 50.0 - 60.0 Hz
|
ASTM D150 | |
| 介电强度 |
14.9 kV/mm
@Thickness 3.20 mm
|
378 kV/in
@Thickness 0.126 in
|
in air; ASTM D149 |
| 耗散因数 |
0.00090
@Frequency 50.0 - 60.0 Hz
|
0.00090
@Frequency 50.0 - 60.0 Hz
|
ASTM D150 |
|
0.010
@Frequency 1.00e+6 Hz
|
0.010
@Frequency 1.00e+6 Hz
|
ASTM D150 | |
| 相比耐漏电起痕指数(CTI) | 250 - 400 V | 250 - 400 V | UL 746A |
| 热丝引燃 (HWI) | 30 - 60 sec | 30 - 60 sec | UL 746A |
| 高电弧燃烧，HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 |
60.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
|
33.3 µin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 |
|
62.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
|
34.4 µin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 | |
|
68.4 µm/m-°C
@Temperature -40.0 - 95.0 °C
|
38.0 µin/in-°F
@Temperature -40.0 - 203 °F
|
ASTM E 831 | |
| 线性热膨胀系数,横向流动 |
57.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
|
31.7 µin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
|
60.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
|
33.3 µin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 比热容 | 1.25 J/g-°C | 0.299 BTU/lb-°F | ASTM C351 |
| 导热系数 | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) |
135 °C
@Thickness 3.20 mm
|
275 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
137 °C
@Thickness 6.40 mm
|
279 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
124 °C
@Thickness 3.20 mm
|
255 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 | |
|
132 °C
@Thickness 6.40 mm
|
270 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 | |
| 维卡软化温度 | 140 °C | 284 °F | Rate B/120; ISO 306 |
| 143 °C | 289 °F | Rate B/50; ISO 306 | |
| 154 °C | 309 °F | Rate B/50; ASTM D1525 | |
| UL RTI | 130 °C | 266 °F | UL 746B |
| UL RTI，机械冲击 | 130 °C | 266 °F | UL 746B |
| UL RTI，机械无冲击 | 130 °C | 266 °F | UL 746B |